ASTM B 150 C63000【鋁青銅C63000產品簡介】
******************************************
鎳鋁青銅,其獨特的綜合性能的高強度,良好的疲勞,優良的耐腐蝕性能在海水中,非引發和磨損特性使其成爲一個受歡迎的選擇整個光譜的行業。
它有非常高的抗磨損性能運行時對大多數等級的鋼和世界基礎上用於航空航天起落架灌木和軸承,其強度、疲勞、耐磨性、耐衝擊性和耐蝕性證明。
化學成分表：
|
Element |
Cu |
Al |
Ni+Co |
Fe |
Mn |
Si |
Sn |
Zn |
|
% |
Bal |
9.0-11.0 |
4.0-5.5 |
2.0-4.0 |
1.5max |
0.25max |
0.2max |
0.3max |
機械性能表：
|
||||||||
|
Form |
Size Range |
Yield 0.2% |
UTS |
Elong % |
Hardness (HB) |
|||
|
Metric |
Imperial |
MPa |
Ksi |
MPa |
Ksi |
% |
(HB) |
|
|
020 |
75-300mm dia |
3- 12” dia |
300-350 |
43.5-50.7 |
600-700 |
87-101 |
12-21 |
180-240 |
|
HR50 |
50-80 mm dia |
2.0- 3.2” dia |
380-430 |
62.3-62.3 |
725-800 |
105-116 |
10-15 |
180-240 |
|
TQ50 |
80-130 mm dia |
3.2 – 5.1” dia |
320- 400 |
46.4-58.0 |
620-770 |
90-111.7 |
15-20 |
180-240 |
020 –Hot forged and annealed, HR50 Drawn and Stress relieved (High Strength) TQ50 Quench hardened and temper annealed.
物理性質AMS 4640
密度- 0.274磅/ in3在68 F
特定的重力- 7.58
電阻率- 116.0 ohms-cmil /英尺@ 68 F
導電率- 7% IACS @ 68 F
鎳鋁青銅的典型使用AMS 4640
-閥莖、泵軸、密封腺體,防噴器部分
,起落架襯套及軸承、皮瓣襯套,致動器,部分,支撐套管
汽車氣門,氣門座
其他工業——球、齒輪、凸輪、軸系、發電站的冷凝器管和脫鹽裝置,氣門座,氣門,泵軸、結構成員,、熱交換器、頭,換熱器法蘭、軸承、軸套、閥球,液壓襯套爲地球移動設備、耐腐蝕的文章,飛機零件、焊接管
它們是QAl5、QAl7、QAl9-2、QAl9-4、QAl9-5-1-1、QAl10-3-1.5、QAl10-4-4、QAl10-5-5、QAl11-6-6.而美國ASTM標準中加工鋁青銅共有26，鑄造合金有18個。鋁青銅的基本合金組成爲Cu-Al、Cu-Al-Fe、Cu-Al-Ni、Cu-Al-Fe-Ni、Cu-Al-Fe-Ni-Mn等。
公司常年備現貨庫存。歡迎各界人士蒞臨參觀指導！！！
UNS No. C95200; UNS No. CuAl10Fe5Ni5-C; UNS No. CuAl10Fe5Ni5-C; UNS No. C95410; UNS No. C95500; UNS No. CuAl10Fe5Ni5-C; UNS No. C95600; UNS No. C95700; UNS No. CuAl10Fe5Ni5-C; UNS No. C95820; and UNS No. C95900.
(In Tension)
|
Imperial |
Metric |
|
|
Density |
0.274lb/in³ @ 68º F |
7580 kg/m³ @ 20ºC |
|
Specific Gravity |
7.58 |
7.58 |
|
Specific Heat |
0.090 Btu/lb º F @68º F |
376.7 J/kg ºC @20 ºC |
|
Electrical Conductivity |
7% IACS @ 68º F |
0.041mega Siemens/cm @20 ºC |
|
Thermal Conductivity |
22.6 Btu.ft(hr.ft² º F) @68º F |
0.391W/cm ºC @20 ºC |
|
Thermal Expansion |
9.0 x10ˉ 6 per º F (68-572 º F ) |
15.5 x10ˉ 6 perºC (20-300 ºC) |
|
Electrical Resistivity |
116Ω-cmil/ft @ 68º F |
19.28 µ Ω-cm@20 ºC |
|
Relative Magnetic Permeability |
1.4µ |
|
|
Machining Index |
20 (Based on free machining brass 100%) |
|
|
Modulus of Rigidity |
6800ksi |
46884MPa |
|
Modulus of Elasticity |
18200ksi |
125484MPa |
|
Melting Range |
1920-1960 ºF |
1049-1071ºC |
|
Hot Working Range |
1450-1700 ºF |
788-927 ºC |
|
Cold Working |
Limited |
|
|
Cryogenic |
Retains properties down to – 302 ºF |
(-190 ºC) |
|
Elevated Temperatures |
Retains properties to 662 ºF |
(350 ºC) |